| Nominal outer Dia. | Minimum Wall Thickness (All sizes in mm) |
|||
| mm | SDR 17.6 | SDR 13.6 | SDR 11.0 | SDR 9.0 |
| 16 | 2.3 | 2.3 | 3.0 | 3.0 |
| 20 | 2.3 | 2.3 | 3.0 | 3.0 |
| 25 | 2.3 | 2.3 | 3.0 | 3.0 |
| 32 | 2.3 | 2.3 | 3.0 | 3.6 |
| 40 | 2.3 | 3.0 | 3.7 | 4.5 |
| 50 | 2.9 | 3.7 | 4.6 | 5.6 |
| 63 | 3.6 | 4.7 | 5.8 | 7.1 |
| 75 | 4.3 | 5.5 | 6.8 | 8.4 |
| 90 | 5.2 | 6.6 | 8.2 | 10.1 |
| 110 | 6.3 | 8.1 | 10.0 | 12.3 |
| 125 | 7.1 | 9.2 | 11.4 | 14.0 |
| 140 | 8.0 | 10.3 | 12.7 | 15.7 |
| 160 | 9.1 | 11.8 | 14.6 | 17.9 |
| 180 | 10.3 | 13.3 | 16.4 | 20.1 |
| 200 | 11.4 | 14.7 | 18.2 | 22.4 |
| 225 | 12.8 | 16.6 | 20.5 | 25.1 |
| 250 | 14.2 | 18.4 | 22.7 | 25.1 |
| Characteristics | Units | Requirements | Test Parameters | Test Methods |
| Conventional Density | kg/m3 | >930(base polymer) | 230C | ISO-1183, ISO-1872/1 |
| Melt Flow rate | G/10min | 0.2 to 1.1 | 1900C/5kg | ISO-4440/1, IS-2530:1963 |
| Thermal Stability | min. | >20 | 2000C | ISO/TR-10837 |
| Hydrostatic Strength | h | Failure time>=100h Failure time>=165h Failure time>=1000h | PE-80-9.0 MPa-200C ; PE-80-4.6 MPa-800C ; PE-80-4.0 MPa-800C | ISO-1167 |
| Elongation at Break | % | >=350 | ISO-6259/3 |